Development of versatile CdMoO4/g-C3N4 nanocomposite for enhanced photoelectrochemical oxygen evolution reaction and photocatalytic dye degradation applications

Abstract

Fabrication of an efficient, stable, and versatile photocatalysts for the energy and environment remediation applications is an urgent task for the current researchers. In this work, we have successfully synthesized a versatile hybrid photocatalysts, i.e.; CdMoO4/g-C3N4 (CMO/CN) by a facile and simple one-pot in-situ hydrothermal method. Here CdMoO4 (CMO) microspheres were deposited on the g-C3N4 (CN) sheets. Fabricated CN, CMO, and CMO/CN composite photocatalysts were analyzed with various characterization techniques like UV–visible diffuse reflectance spectra (UV–Vis DRS), photoluminescence spectroscopy (PL), time-resolved fluorescence lifetime (TRFL), electrochemical impedance spectroscopy (EIS), powder X-ray diffraction (PXRD), Fourier transform infrared spectroscopy (FT-IR), Scanning electron microscopy–energy-dispersive X-ray analysis (SEM-EDX), transmission electron microscope (TEM), thermogravimetric analysis (TGA), X-ray photoelectron spectroscopy (XPS), and Brunauer–Emmett–Teller (BET). The results reveal that the formation of a strong heterojunction between two semiconductors leads to the formation of active photocatalyst. Furthermore, as-synthesized materials were tested for the photoelectrocatalytic (PEC) oxygen evolution reactions (OERs) in acidic medium, and photocatalytic (PC) degradation of methylene blue (MB) under light irradiation. Among all tested samples, CMO/CN-10 has shown the highest current density 52.74 mA cm−2 at 1.95 V with lowest over potential of 0.70 mV on glassy carbon electrode for OER in acidic medium under the light irradiation. The PC degradation rate constant of CMO/CN-10 composite in MB solution is k = 2.0 × 10−2 min−1, whereas for the pure CMO and CN degradation rate constant is k = 5.7 × 10−3 min−1 and k = 1.2 × 10−2 min−1, respectively. This enhancement in PEC and PC properties is due to the fast migration of photo-induced electrons in the case of CMO/CN-10 nanocomposite. Trapping experiment results reveal the major reactive species for PC degradation of MB is •OH (hydroxyl radicals) and h+ (holes), respectively, and suitable PC reaction mechanism also proposed for CMO/CN-10 composites. Based on the above remarkable results, it would be a potential nanocomposite for the PEC oxygen evolution and PC degradation of MB under light illumination.