Abstract
Spin valves composed of ferrimagnetic/Cu/ferrimagnetic layers were fabricated with the magnetization perpendicular to the film planes. By changing the composition of ferrimagnetic layers, both negative and positive giant magnetoresistance (GMR) can be observed in ferrimagnetic spin valves. For samples consisting of both transition-metal (TM-) rich TbFeCo and GdFeCo, negative GMR values were obtained. Due to the high resistivity of amorphous ferrimagnetic films, the shunting effect of Cu led to relatively small MR ratio. The negative MR effect was 1% for 1.7 nm Cu. For spin valves consisting of rare-earth (RE-)rich TbFeCo and TM-rich GdFeCo, positive GMR values were observed. A thin layer of Co was inserted between RE-rich TbFeCo and Cu to manipulate the sign of GMR.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.