Abstract
Porous lead zirconate titanate (PZT) ceramics with three‐dimensionally interconnected pores were prepared using a novel tert‐butyl alcohol‐based gel‐casting process, an unconventional technique in acquiring high‐porosity ceramics. In the present work, PZT ceramics with porosity ranging from 31.3% to 58.6% were fabricated by adjusting the initial solid loading and sintering temperature. The fabricated samples were characterized in terms of both porous structure and functional properties to clarify the underlying correlation. With the increase of porosity, relative permittivity (ɛr) decreased to a significantly low value compared with dense PZT ceramics while the longitude piezoelectric coefficient (d33) exhibited a moderate decline, which could be attributed to the unique structure with homogeneous pore distribution. As a result, the resultant samples possessed a high value of hydrostatic figure of merit, >100 times higher than that of dense materials. The acoustic impedance (Z) showed a linear dependence on porosity with the lowest magnitude reaching 3.0 MRayls (106 kg·(m2·s)–1), hopefully leading to enhanced coupling with biological tissue or water.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.