Abstract
The crosslinking reaction of pure poly(acrylic acid) and its blend with poly(vinyl alcohol) was studied by FT-IR spectroscopy. It is demonstrated that also in blends the anhydride formation characteristic for pure poly(acrylic acid) is the predominant crosslinking reaction upon heating. But the ester formation between poly(vinyl alcohol) and poly(acrylic acid) is detectable due to the ester C=O vibrations and C—O—C vibrations, respectively. The degree of swelling and the Young's modulus of the crosslinked blend in deionized water depend on the time and temperature of the heat treatment. In dependence of the pH-value of the swelling agent the blends swell or shrink. The working energy at the shrinking or swelling process induced by a change of the pH-value of differently treated blends was measured. The values are in a range of technical interests and comparable with other microactuators.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.