Abstract
The electrochemical synthesis of poly(o-anisidine) (POA) was achieved on brass (CuZn) electrode by ap- plying two scan rates (50 and 20 mVs −1 ). The synthesized polymer films were strongly adherent and homogeneous in both cases. Their corrosion performance was investigated by AC impedance spectroscopy (EIS) technique, anodic polarization plots and open circuit potential-time curves, in 3.5% NaCl solution. It was clearly seen that poly(o-anisidine) films provided a significant physical protection for longer exposure time. It was shown that polymer film coated at high scan rate (CuZn/POA-H) exhibited better barrier property against the attack of corrosive agents when compared with polymer film obtained at low scan rate (CuZn/POA-L). It was found out that poly(o-anisidine) film synthesized at high scan rate caused a significant increase in corrosion resistance by its catalytic behavior on formation of protective oxide layers on the surface in longer time.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.