Abstract
Photo-induced hardening, substructure formation and damage of C 60 single crystals under the 632.8 nm He-Ne laser irradiation in air at a power density of 1.47 mW/mm 2 was investigated by microhardness and AFM methods. Photo-induced formation of the dislocation substructure and crystallographically oriented crack patterns on the (111) face due to lattice contraction on polymerization were observed. Two phototransformed states: soft (400-450 MPa) and hard (650-1000 MPa) are found to appear under laser-irradiation. Hard fullerite is created in the subsurface layer < 1 μm at the saturation stage of phototransformation. It softens to 400-450 MPa at 340 K and reverts to non-polymerized state at 470-480 K. The effect of post-irradiation hardening, which appears as an increase of the hardness of laser-irradiated crystals after storage in air in the dark, has been discovered.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.