Abstract
This study focuses on developing an active and biodegradable packaging using electrospinning, with polylactic acid (PLA) as the matrix and bamboo leaf extract (BLE) as the antioxidant compound. The research systematically evaluates the relationship among process parameters, material properties, and structure. The electrospun membranes were produced using different BLE contents (10 wt%, 20 wt%, 30 wt%, and 40 wt%) and characterized by their morphology, mechanical properties, wettability, and antioxidant activity. Scanning electron microscopy (SEM) revealed BLE’s influence on fiber morphology, with a slight increase in diameter in PLA/BLE at 10% and 20%, attributed to higher viscosity. Conversely, PLA/BLE 30% and 40% showed a mild reduction in fiber diameter likely due to polyphenols’ capacity to enhance PLA chain mobility. Mechanical tests indicated proportional reductions in modulus, maximum stress, and strain at break, upon increasing the BLE concentration, although these parameters are still suitable for packaging applications. The decrease in modulus is attributed to polyphenol capacity to increase PLA chain mobility, while increased fragility results from embedded particles acting as local defects. Wettability tests demonstrated increased hydrophilicity with higher BLE content. Total polyphenol content, estimated through FOLIN assay, increased proportionally with incorporated BLE, impacting antioxidant properties assessed via FRAP assay.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.