Polyimides 7: Synthesis, characterization, and properties of novel soluble semifluorinated poly(ether imide)s

Abstract

AbstractThree novel diamine monomers (VI, VII, and VIII) were synthesized. These diamine monomers lead to a number of semifluorinated poly(ether imide)s when reacted with different commercially available dianhydrides like pyromellitic dianhydride (PMDA), benzophenone tetracarboxylic acid dianhydride (BTDA), 2,2‐bis (3,4‐dicarboxyphenyl) hexafluoropropene (6FDA), and oxydiphthalic dianhydride (ODA) by thermal imidization route. Elemental analyses, IR and NMR techniques were used to characterize the monomers and polymers. The resulting polymers exhibited weight average molar masses up to 1.78 × 105 g mol−1 in GPC with respect to polystyrene standard and have very good solubility in several organic solvents such as NMP, DMF, DMAC, DMSO, chloroform, and THF. Very good solubility of these polymers in CDCl3 enables their complete characterization by proton as well as 13C‐NMR techniques. The polymers showed very high thermal stability with decomposition temperature (5% weight loss) up to 511°C in air and high glass transition temperature up to 311°C depending upon the exact repeating unit structure. The polymer films showed high modulus (up to 2.9 GPa) as was evaluated by DMA. The polymers also showed very low water absorption (0.16%), low dielectric constant (2.35 at 1MHz) and very good optical transmission. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 3025–3044, 2007