Abstract
To address the inferior mechanical properties associated with high phosphoric acid (PA) content, a rigid microporous polymer containing carboxyl groups (cPIM) was incorporated into poly (triphenylene-piperidine) (PTP) matrix to prepare composite membranes (PTP-xcPIM) for high-temperature proton exchange membrane fuel cells (HT-PEMFCs). Compared to the original membrane (PTP/PA), the PTP-xcPIM/PA reinforced membranes exhibited improved mechanical properties (13–17 MPa) and higher proton conductivity (>90 mS cm−1@180 °C) at a similar PA content. After assembling into a single HT-PEMFC, the reinforced composite membrane could achieve a high output power of over 1000 mW cm−2. The addition of the microporous layer to the composite membranes significantly increased the PA retention due to its siphoning effect on PA. Especially, PTP-10cPIM/PA retained 57.64% of PA after 100 h at 60 °C and 50%RH, while PTP/PA retained only 52.11% in the same harsh environment. These phenomena imply that the strategy of introducing rigid microporous polymers containing functional groups can lead to the simultaneous enhancement on the PA retention capacity and proton conductivity at low PA doping levels, and effectively avoid the “trade-off” effect between the mechanical properties and the output performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.