Abstract
Rechargeable aqueous Zn metal batteries are promising candidates for renewable energy storage. However, Zn metal is chemically active and suffers from chemical corrosion in aqueous electrolyte due to its low redox potential. It is of vital importance to reveal the corrosion mechanism, and improve the chemical stability and electrochemical reversibility of Zn metal anode for its practical application. In this work, it is revealed that a Zn metal electrode readily gets oxidized during its resting in aqueous ZnSO4 electrolyte, forming zinc hydroxide sulfate and hydrogen gas, leading to the increased internal resistance and swollen problems of batteries, and eventually battery failure. To inhibit such chemical corrosion, an anti-corrosive metallic Cu is introduced to Zn metal anode to construct a uniform Cu/Zn composite with dense structure, which is electrochemically converted to Cu–Zn alloy/Zn composite during battery cycling. The as-achieved Cu–Zn/Zn electrode exhibits stable cycling for over 1500 cycles at 1 mA/cm2 and 0.5 mAh/cm2 with little change in overpotential (46 mV) after resting for 1 month, while the bare Zn electrode shows large voltage fluctuation and high overpotential (>400 mV) under the same condition, suggesting the importance of inhibiting the chemical corrosion of Zn metal anode for rechargeable aqueous batteries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.