Plasmonic Effects of Infiltrated Silver Nanoparticles Inside TiO2 Film: Enhanced Photovoltaic Performance in DSSCs

Abstract

The plasmonic effects of infiltrated silver (Ag) nanoparticles, with different contents, inside a nanostructured TiO2 film on the photovoltaic performance of dye‐sensitized solar cells (DSSCs) are explored. The synthesized Ag nanoparticles are immobilized onto deposited TiO2 nanoparticles by a new strategy using 3‐mercaptopropionic acid (MPA), a bifunctional linker molecule. Transmission electron microscope (TEM) images show that monodispersed Ag and polydispersed TiO2 nanoparticles have an average diameter of 12 ± 3 nm and 5 ± 1 nm, respectively. Moreover, Fourier transform infrared spectroscopy (FTIR) analysis reveals that Ag nanoparticles were successfully functionalized and capped with MPA. Optical studies on the MPA‐capped Ag nanoparticles inside TiO2 film show an increase in the total absorbance of the electrode. Moreover, EIS measurements confirm that MPA‐capped Ag nanoparticles inhibit the charge recombination and improve the stability of nanoparticles in I3−/I− electrolyte. The DSSC assembled with optimal content of MPA‐capped Ag nanoparticles demonstrated an enhanced power conversion efficiency (8.82% ± 0.07%) compared with the pure TiO2 (7.30% ± 0.05%). The increase in cell efficiency was attributed to the enhanced dye light absorption in strength and spectral range due to the surface plasmon resonance of MPA‐capped Ag nanoparticles in the photoanode.