Abstract
Abstract High-resolution transmission electron microscopy, electron diffraction and parallel electron-energy-loss spectroscopy are used to analyse nanocrystalline diamond powder. Grains of diameter in the range 2–10 nm were found aggregated together; the grain boundaries were essentially a grossly disordered (amorphous) intergranular phase. Analysis of the plasmon loss function indicated a mass density of 3·30 g cm−1, compared with 3·51 g cm−3 for a chemically vapour-deposited diamond. The core loss spectra showed virtually pure sp3 bonding overall although some exposed surfaces were coated with two or three graphitic layers. Two peaks were observed in the low energy loss function; one at 34 eV was characteristic of the volume plasmon typically observed in crystalline diamond, and a second peak at approximately 23 eV for larger grains shifted to lower energies as the particle size decreased (to 19·5 eV for 2·8 nm diameter) and at the same time increased in intensity, becoming stronger than the volume plas...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.