Abstract
Low dielectric constant SiOC(–H) thin films were deposited by plasma enhanced chemical vapor deposition (PECVD) using methyltriethoxysilane (MTES) and oxygen as precursors. The SiOC(–H) films were prepared with MTES/O 2 flow rate ratio of 80%, rf power of 700 W and the working pressure was varied from 110 to 150 mTorr. Then the films were annealed at different temperatures in an Ar ambient for 30 min in order to study their thermal stability. Film thickness and refractive index were measured by SEM and ellipsometry, respectively. Bonding characteristics of the films were investigated by Fourier transform infrared (FTIR) spectroscopy. The dielectric constant of SiOC(–H) film was evaluated by C– V measurements using Al/SiOC(–H)/ p-Si structure. The dielectric constants as low as 2.4 have been obtained for the film annealed at 500 °C with the working pressure of 150 mTorr. The annealing treatment was found to reduce dielectric constant significantly due to abundant incorporation of methyl group into the Si–O network. These results demonstrated the promising characteristics of SiOC(–H) thin films deposited by using oxygen and MTES precursor.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.