Abstract
The purpose of this study was to determine the flexural strength (FS), flexural modulus (FM), depth of cure (DC), polymerization shrinkage (PS), and microhardness (VH) of the following composites: Two packable composites--Filtek P-60 and Solitaire 2; One ion-releasing composite--riston AT; and Two hybrid composites--Charisma and Filtek Z-250. Data of the different tests conducted were obtained as follows: FS and FM data were determined with a universal-testing machine; Polymerization shrinkage was determined using the apparatus of Watts and Cash; Depth of cure was measured with a micrometer (Mitotuyo, UK); and Microhardness was measured with a Shimadzu Microhardness tester (500 g, 15 seconds). All data of the different tests were statistically analyzed by one-way variance analysis (ANOVA), which yielded the following results: Filtek Z-250 showed the statistically highest flexural strength and modulus values. Solitaire 2 exhibited the highest shrinkage, while the volumetric shrinkage results of Filtek Z-250 and Filtek P-60 ranked the lowest. For depth of cure, there were no statistically significant differences among all materials tested (p<0.05). Microhardness results revealed the following tendency: Filtek Z-250 = Filtek P-60 > Ariston AT = Solitaire 2 = Charisma.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.