Physical Properties of an Acrylic Resin after Incorporation of an Antimicrobial Monomer

Abstract

This study evaluated the effect of the incorporation of the antimicrobial monomer methacryloyloxyundecylpyridinium bromide (MUPB) on the hardness, roughness, flexural strength, and color stability of a denture base material. Ninety-six disk-shaped (14-mm diameter × 4-mm thick) and 30 rectangular (65 × 10 × 3.3 mm(3) ) heat-polymerized acrylic resin specimens were divided into three groups according to the concentration of MUPB (w/w): (A) 0%, (B) 0.3%, (C) 0.6%. Hardness was assessed by a hardness tester equipped with a Vickers diamond penetrator. Flexural strength and surface roughness were tested on a universal testing machine and a surface roughness tester, respectively. Color alterations (ΔE) were measured by a portable spectrophotometer after 12 and 36 days of immersion in water, coffee, or wine. Variables were analyzed by ANOVA/Tukey HSD test (α= 0.05). The following mean results (±SD) were obtained for hardness (A: 15.6 ± 0.6, B: 14.6 ± 1.7, C: 14.8 ± 0.8 VHN; ANOVA: p= 0.061), flexural strength (A: 111 ± 17, B: 105 ± 12, C: 88 ± 12 MPa; ANOVA: p= 0.008), and roughness (A: 0.20 ± 0.11, B: 0.20 ± 0.11, C: 0.24 ± 0.08 μm; ANOVA: p= 0.829). Color changes of immersed specimens were significantly influenced by solutions and time (A: 9.1 ± 3.1, B: 14.8 ± 7.5, C: 13.3 ± 6.1 ΔE; ANOVA: p < 0.05). The incorporation of MUPB affects the mechanical properties of a denture base acrylic resin; however, the only significant change was observed for flexural strength and may not be critical. Color changes were slightly higher when resin containing MUPB was immersed in wine for a prolonged time; however, the difference has debatable clinical relevance.