Abstract
TbPdAl2 and the solid solution Tb1-xLuxPdAl2 (x = 0.1-1) have been synthesized via arc-melting techniques using the elements as starting materials and crystallize in the orthorhombic MgCuAl2-type structure (Cmcm). As expected, the unit cell volumes decrease due to the lanthanide contraction from the Tb to Lu compounds, thus showing Vegard behavior because of the differences of the ionic radii of the trivalent rare-earth cations. TbPdAl2 orders ferromagnetically below TC = 85.5(5) K and shows partial magnetic saturation already at low fields. The magnetic phase transition has been additionally investigated by heat capacity measurements, showing a broadened λ anomaly at THC = 83.2(1) K. The electrical resistivity is almost linear above TC, indicating dominant electron-phonon interactions. Below the ordering temperature, electron-spin wave scattering with a ρ ∼ T2 behavior is evident. In the solid solution Tb1-xLuxPdAl2 (x = 0-1), the ferromagnetic Curie temperatures decrease in a linear fashion with increasing Lu content. Investigations of the magnetocaloric properties of TbPdAl2 obtained a maximum magnetic entropy change of -ΔSMmax = 1.2, 2.2, 3.1, and 3.6 J kg-1 K-1 for the field changes of ΔH = 10, 20, 50, and 70 kOe, respectively. The rather low values are caused by entropy losses due to hysteresis behavior. The relative cooling power for TbPdAl2, therefore, also exhibits comparably low values of 32, 81, 142, and 178 J kg-1.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.