Abstract
AbstractThe physical aging behavior of nylon 66 as a function of aging temperature, magnitude of applied stress, and aging time has been investigated. Creep tests were performed for samples quenched from a stabilization temperature of 160°C to aging temperatures between 41°C and 65°C, for aging times ranging from 0.5 to 64 h, and at stresses levels from 4 MPa to 24 MPa. Volume recovery was investigated for samples quenched from 160°C to aging temperatures of 41°C and 65°C. The creep compliance curves at different aging times were able to be superimposed. The double logarithmic shift rate was calculated and its dependence on aging temperature and applied stress was determined. Also, it was found that the volume recovery rate depends on the aging temperature. The time‐temperature and stress‐temperature superpositions were not possible for our data.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.