Abstract

A narrow band photoluminescence (PL) emission peak resulting from CdS-Au solid solution was observed when growing one-dimensional nanostructures of CdS via the vapor-liquid-solid mechanism by using Au as the catalyst. This emission peak was located at 680 nm, a wavelength longer than the near band edge emission of CdS at 520 nm, and was shown not to be caused by the usual trap states of CdS which lead to a broad band emission. Here, the one-dimensional nanostructures of CdS were grown in a simple, low-temperature (360 degrees C) metal-organic chemical vapor deposition process with a single source precursor of CdS. Straight nanowires of diameter 50-70 nm and wormlike nanorods of diameter 100-200 nm were obtained. Both the upper and lower portions of the nanorods/nanowires possessed single crystallinity as judged from the corresponding high-resolution transmission electron microscopy images and selected area electron diffraction data. This work demonstrates the feasibility of adjusting PL emission peaks of optoelectronic semiconductors through alloying with metals.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call