Abstract
Cerium-doped yttrium aluminium garnet (Y 3Al 5O 12, YAG) microcrystals were grown using sol–gel technique. The samples were characterized by application of X-ray diffraction (XRD), photoluminescence (PL) spectroscopy and frequency-domain fluorescence lifetime measurements. The PL output, which is important for wavelength conversion in white light emitting diodes (LEDs), was studied as a function of Ce content and annealing temperature. XRD analysis evidenced that sintering of polycrystalline Y 3Al 5O 12:Ce powders at 1000 °C results in the formation of monophasic garnet materials up to 10 mol% of Ce doping; however, concentration quenching is observed in samples with the Ce content exceeding ∼4% probably due to optical losses in the tail states of the imperfect lattice. PL output increased and the concentration quenching disappeared when a higher sintering temperature of 1300 °C was used. However, in high Ce content (>4%) samples, the increase in sintering temperature was found to result in the formation of CeO 2 phase accompanied by an uncontrolled bouncing of PL intensity in powders with similar Ce content.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.