Abstract
In this study, we investigated the phase transitions and thermoelectric properties of charge-compensated hakite (ZnxCu12-xSb4Se13) as a function of Zn content. Based on X-ray diffraction and a differential scanning calorimetric phase analysis, secondary phases (permingeatite and bytizite) transformed into hakite depending on the Zn content, while Zn2Cu10Sb4Se13 existed solely as hakite. Nondegenerate semiconductor behavior was observed, exhibiting increasing electrical conductivity with a rising temperature. With an increase in Zn content, the presence of mixed phases of hakite and permingeatite led to enhanced electrical conductivity. However, Zn2Cu10Sb4Se13 with a single hakite phase exhibited the lowest electrical conductivity. The Seebeck coefficient exhibited positive values, indicating that even after charge compensation (electron supply) by Zn, p-type semiconductor characteristics were maintained. With the occurrence of an intrinsic transition within the measured temperature range, the Seebeck coefficient decreased as the temperature increased; at a certain temperature, Zn2Cu10Sb4Se13 exhibited the highest value. Thermal conductivity showed a low temperature dependence, obtaining low values below 0.65 Wm-1K-1. A power factor of 0.22 mWm-1K-2 and dimensionless figure of merit of 0.31 were achieved at 623 K for ZnCu11Sb4Se13.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.