Abstract
ABSTRACT The inorganic multiferroic compounds Bi0.9Sm0.1Fe1 − x V x O3 (x = 0.0, 0.015, 0.03, and 0.045) were prepared by the solid-state reaction method. X-ray diffraction analysis confirmed the rhombohedral perovskite-like structure with minor traces of the impurity phases Bi2Fe4O9 and Bi25FeO40. The lattice parameters a and c, and the volume of the hexagonal unit cell were extracted from the X-ray diffraction data and found to increase as the V5+ content is increased. The average crystallite size was estimated to be in the range 380–415 Å. Fourier transform infrared spectroscopy confirmed the rhombohedral perovskite-like structure via the vibration bands of the octahedral FeO6 group observed between 410 and 570 cm−1. A differential scanning calorimeter was used to record the thermal scans which revealed that the compounds have undergone crystalline phase transitions at temperatures in the range 300–320°C. A 4.5% V + 5 substitution has shifted the transition peak by 20°C. The magnetic hysteresis loops taken at room temperature with a vibrating sample magnetometer revealed the ordinary ferromagnetic behavior. The V5+ substitution enhanced the remanent magnetization, but the magnetic coercivity was found to fluctuate around an average value of about 1000 Oe. The compound Bi0.9Sm0.1Fe0.955V0.045O3 exhibited the maximum remanent magnetization.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.