Phase modification of copper phthalocyanine semiconductor by converting powder to thin film

Abstract

Abstract Thin films of copper phthalocyanine (CuPc) semiconductor were deposited on glass substrates by a thermal evaporation system using the CuPc powder in a high vacuum. The crystal structures of both the films and the powder were measured by the X-ray diffraction spectroscopy technique. It is observed that CuPc films only show one peak at 6.84°, indicating a high texture of α phase along (200) orientation. In comparison, CuPc powder shows a series of peaks, which are confirmed from the mixture of both α and β phases. The effects of substrate anneal temperature on the film structure, grain size and optical absorption property of CuPc films were also investigated. All the films are of α phase and the full width of half maximum for (200) diffraction peak becomes narrow with increasing the substrate temperatures. The average grain size calculated by the Scherrer’s formula is 33.63 nm for the film without anneal, which is increased up to 58.29 nm for the film annealed at 200 °C. Scanning electron microscope was further measured to prove the growth of crystalline grain and to characterize the morphologies of CuPc films. Ultraviolet-visible absorption spectra were employed to study the structure effect on the optical properties of both CuPc films and powder. Fourier Transform infrared spectroscopy was used to identify the crystalline nature of both CuPc powder and film.