Abstract
Summary Permeable cement has been widely used in the construction industry. In oil fields, the use of permeable cement to replace screens and reduce the cost of well construction has been attempted. However, the compressive strength of permeable cement is low. Herein, a new method for producing permeable cement using foamed cement and permeable microspheres (PMs) is proposed. A permeable cement slurry system is produced by selecting the foaming agent, foam stabilizer, length and dosage of basalt fibers, and permeable skeleton materials (PSMs). The system formula is Jiahua G-grade cement + 1.3% alpha-olefin sulfonate (AOS) + 0.5% xanthan gum (Xg) + 2% nano-SiO2 + 1% 6-mm basalt fiber + 30% PM. The compressive strength and permeability of the permeable cement were tested using compressive strength and hydraulic permeability tests, respectively. The compressive strength of this system could reach 6.6 MPa when it was cured for 2 days at 50°C. Its liquid permeability could reach 0.06×10−3 μm2 when it was cured for 14 days at 50°C.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call