Abstract
Due to the carbon dioxide emission arising from the production of cement, alternative concrete that is environmentally friendly such as metakaolin geopolymer concrete have been developed. However, the performance of metakaolin based geopolymer concrete (MKGC) when exposed to aggressive environment particularly elevated temperature has not been investigated. Therefore, this paper assessed the performance of MKGC exposed to elevated temperatures. MKGC cube specimens of grade 25 were produced using a mix ratio of 1:1.58:3.71.After preparing the specimens, they were placed in an electric oven at a temperature of 60oC for 24 hours. Thereafter, the specimens were stored in the laboratory at ambient temperature for 28 days. The specimens were then exposed to elevated temperatures of 200, 400, 600 and 800oC. After exposure to elevated temperatures, the MKGC specimens were subjected to compressive strength, water absorption and abrasion resistance tests. Results show that at 600 and 800oC, the MKGC lost a compressive strength of 59.69% and 71.71% respectively. Higher water absorption and lower abrasion resistance were also observed.
 Keywords: Cement, Compressive Strength, Metakaolin Concrete, Elevated Temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.