Abstract
<p>Ba<sub>0,8</sub>Sr<sub>0,2</sub>TiO<sub>3 </sub>was made by co-precipitation method with the sintering temperature of 600<sup>o</sup>C, 700<sup>o</sup>C, 800<sup>o</sup>C and 900<sup>o</sup>C for 4 hours. Sintering temperature was varied to investigate its effect on microstructure and dielectric constant of Ba<sub>0,8</sub>Sr<sub>0,2</sub>TiO<sub>3</sub>. microstructure characterization was performed by X-Ray Diffraction (XRD) instrument. Dielectric constant characterization was perform by LCR meter. The crystal size increased significantly with increasing sintering temperature. Measurements of dielectric constant were performed at range of frequency 0.01 to 100 KHz. Dielectric constant value is highest at the lowest frequency. Dielectric constant value size increased significantly with increasing sintering temperature.</p>
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.