Abstract
Friction stir welding is a solid-state welding process used extensively for aluminium alloys. EN AW-1100 alloy is mostly used for its exceptional corrosion resistance, high ductility, high thermal and electrical conductivities, and cost-effectiveness. This study is focused on the optimisation of friction stir welding parameters to achieve enhanced mechanical properties of 5mm thick EN AW-1100 alloy plates welded with a single pass, using Taguchi L9 orthogonal array and ANOVA analysis. Experimental results revealed that maximum tensile strength of 79 MPa and percentage elongation of 38.87 % were achieved. The maximum Vickers hardness achieved in the stir zone was 34.15. These results were used for optimisation using Minitab and it was determined that 2000 RPM, 30 mm·min−1 traverse speed and square probe profile came out to be the best parameters for maximum tensile strength. 4000 RPM, 30 mm·min−1 traverse speed and square probe geometry were the best parameters for maximum hardness in the stir zone. ANOVA analysis showed that the most significant parameter for tensile strength was traverse speed. None of the considered parameters were influencing the hardness value in the stir zone at a 95 % confidence level.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.