Abstract
AbstractPorous bioactive glass (BaG) structures were manufactured applying novel preceramic paper process. Preceramic papers were produced for aqueous suspensions loaded with different contents of pulp fiber and BaG filler. Pressure loading was applied in order to increase the packing density in the paper sheets. The paper sheets were sintered at 630 °C for 1 h. The porous glass–ceramic specimens were characterized for density, porosity, composition, microstructure, and mechanical properties. A pronounced volumetric shrinkage was observed, but no surface flaws or inhomogeneous areas were detected. The mechanical strength using the ball on three balls test and elastic modulus of sintered specimens vary between 21 and 33 MPa and 0.30–0.85 GPa, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.