Oxygen vacancy modulated optical and dielectric properties of photoactive γ-Fe2WO6

Abstract

Ferrite compounds have gained scientific attention for their multifunctional attributes. This investigation explores the structural, optical, dielectric and conductivity properties of polycrystalline γ-Fe2WO6 synthesized by the solid state route. The X-ray diffraction confirmed the orthorhombic structure and single-phase formation, while the electron microscopy showed uniform distribution of dense micrometer-sized grains in γ-Fe2WO6. The FTIR spectroscopy analysis validated the presence of active stretching and bending modes, signifying oxygen anion vibration at both Fe and W sites. The simultaneous presence of Fe2+ and Fe3+ ions in the matrix, as confirmed by X-ray photoelectron spectroscopy (XPS), results in an augmented optical energy band gap and contributes to dielectric permittivity due to the charge carrier hopping mechanism between the trap sites. The compound manifests semiconductor attributes, evident in its indirect optical band gap measuring 1.7 eV. It is observed that the compound has effectively degraded the Methylene Blue (MB) under the visible light within 40 min with a degradation efficiency up to 63 %. The material's electrical conductivity, follows the Jonscher's power law, signifies its semiconductor nature and adheres to the Small Polaron tunneling model for charge conduction between neighboring sites. The impedance (Z′) curves exhibit dielectric relaxation (≤ 10 kHz) with a similar activation energy to the dc conductivity study. The activation energy, determined from both the impedance and conductivity analyses, indicates a connection with the migration of oxygen vacancies within the material. Our observation reveals the presence of oxygen vacancies, which possibly act as in-gap electron traps, enhancing the correlated optical and ac conductivity properties, making it an appealing material for diverse multifunctional applications.