Abstract
Oxygen ion conduction in Nd3+‐doped Pb(ZrxTi1−x)O3 (PZT) was investigated by impedance spectroscopy and 18O‐tracer diffusion with subsequent secondary ion mass spectrometry (SIMS) analysis. Ion blocking electrodes lead to a second relaxation feature in impedance spectra at temperatures above 600°C. This allowed analysis of ionic and electronic partial conductivities. Between 600°C and 700°C those are in the same order of magnitude (10−5–10−4 S/cm) though very differently activated (2.4 eV vs. 1.2 eV for ions and electron holes, respectively). Oxygen tracer experiments showed that ion transport mainly takes place along grain boundaries with partly very high local ionic conductivities. Numerical analysis of the tracer profiles, including a near‐surface space charge zone, revealed bulk and grain‐boundary diffusion coefficients. Calculation of an effective ionic conductivity from these diffusion coefficients showed good agreement with conductivity values determined from impedance measurements. Based on these data oxygen vacancy concentrations in grain boundary and bulk could be estimated. Annealing at high temperatures caused a decrease in the grain‐boundary ionic conductivity and onset of additional defect chemical processes near the surface, most probably due to cation diffusion.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.