Oxidative degradation of industrial wastewater using spray deposited TiO2/Au:Fe2O3 bilayered thin films

Abstract

The Fe2O3, Au:Fe2O3, TiO2/Fe2O3 and TiO2/Au:Fe2O3 thin films are successfully prepared by the spray pyrolysis technique at an optimised substrate temperature of 400°C and 470°C, respectively onto amorphous and F:SnO2 coated glass substrates. The effect of TiO2 layer onto photoelectrochemical (PEC), structural, optical and morphological properties of Fe2O3, Au:Fe2O3, TiO2/Fe2O3 and TiO2/Au:Fe2O3 thin films is studied. The PEC characterization shows that, maximum values of short circuit current (Isc) and open circuit voltage (Voc) are (Isc=185μA and Voc=450mV) are at 38nm thickness of TiO2. Deposited films are polycrystalline with a rhombohedral and anatase crystal structure having (104) preferred orientation. SEM and AFM images show deposited thin films are compact and uniform with seed like grains. The photocatalytic activities of the large surface area (64cm2) TiO2/Au:Fe2O3 thin film photocatalysts were evaluated by photoelectrocatalytic degradation of industrial wastewater under sunlight light irradiation. The results show that the TiO2/Au:Fe2O3 thin film photocatalyst exhibited about 87% and 94% degradation of pollutant in sugarcane and textile industrial wastewater, respectively. The significant reduction in COD and BOD values from 95mg/L to 13mg/L and 75mg/L to 11mg/L, respectively was also observed.