Abstract
The surface and in-depth compositions of sputter-deposited Cu0.57Ni0.42Mn0.01 thin films were studied by Auger electron depth profiling after thermal treatment. The samples were thermally cycled to maximum temperatures of 300 °C to 550 °C in air, argon and forming gas (N2, 5 vol. % H2). Linear least-squares fit to standard spectra and factor analysis were applied to separate the overlapping Auger transitions of Cu and Ni. Under bombardment by 4 keV argon ions, CuNi(Mn) layers display bombardment-induced surface enrichment of Ni in the same extent as binary CuNi alloys. At sufficiently high oxygen partial pressures, a duplex oxide layer is formed and a thick surface copper oxide overgrows the initial nickel oxide. In reducing atmosphere selective oxidation of manganese takes place. A capping NiCr layer prevents CuNi(Mn) from being oxidized, but the film configuration is degraded with increasing annealing temperature due to formation of a surface chromium oxide and diffusion of Ni from the CuNi(Mn) layer into the NiCr/CuNi(Mn) interface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.