Abstract
A novel laminated TiAl matrix composite (LMC) consisting of alternating equiaxed grain layers (EGLs) and fully lamellar grain layers (FGLs) has been fabricated successfully by hot pressing of alternating Ti/Al–6Si foils and subsequent multi-step reaction annealing. The oxidation behavior of the LMC at 800 °C was studied. The results show that the oxide scale is formed with typical multilayer structure after oxidized at 800 °C for 100 h. The oxidation behavior is different between EGLs and FGLs while the thickness of oxide scale is almost identical, suggesting an isotropy oxidation resistance of the LMC. Si addition effectively enhances the oxidation resistance of the LMC.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.