Abstract
AbstractThe electronic structure of the interfaces formed after deposition of MoO3 hole‐injection layers on top of a polymer light‐emitting material, poly(dioctylfluorene‐alt‐benzothiadiazole) (F8BT), is studied by ultraviolet photoelectron spectroscopy (UPS), X‐ray photoelectron spectroscopy and metastable atom electron spectroscopy. Significant band bending is induced in the F8BT film by MoO3 “acceptors” that spontaneously diffuse into the F8BT “host” probably driven by kinetic energy of the deposited hot MoO3. Further deposition leads to the saturation of the band bending accompanied by the formation of MoO3 overlayers. Simultaneously, a new electronic state in the vicinity of the Fermi level appears on the UPS spectra. Since this peak does not appear in the bulk MoO3 film, it can be assigned as an interface state between the MoO3 overlayer and underlying F8BT film. Both band bending and the interface state should result from charge transfer from F8BT to MoO3, and they appear to be the origin of the hole‐injection enhancement by the insertion of MoO3 layers between the F8BT light‐emitting diodes and top anodes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.