Abstract
Porous anodic alumina (PAA) is a well-defined material that has found many applications. The range of applications toward sensing and recognition can be greatly expanded if the alumina surface is covalently modified with an organic monolayer. Here, we present a new method for the organic modification of PAA based on the reaction of terminal alkynes with the alumina surface. The reaction results in the the formation of a monolayer within several hours at 80 °C and is dependent on both oxygen and light. Characterization with X-ray photoelectron spectroscopy and infrared spectroscopy indicates formation of a well-defined monolayer in which the adsorbed species is an oxidation product of the 1-alkyne, namely, its α-hydroxy carboxylate. The obtained monolayers are fairly stable in water and at elevated temperatures, as was shown by monitoring the water contact angle. Modification with 1,15-hexadecadiyne resulted in a surface that has alkyne end groups available for further reaction, as was demonstrated by the subsequent reaction of N-(11-azido-3,6,9-trioxaundecyl)trifluoroacetamide with the modified surface. Biofunctionalization was explored by coupling 11-azidoundecyl lactoside to the surface and studying the subsequent adsorption of the lectin peanut agglutinin (PNA) and the yeast Candida albicans, respectively. Selective and reversible binding of PNA to the lactosylated surfaces was demonstrated. Moreover, PNA adsorption was higher on surfaces that exposed the β-lactoside than on those that displayed the α anomer, which was attributed to surface-associated steric hindrance. Likewise, the lactosylated surfaces showed increased colonization of C. albicans compared to unmodified surfaces, presumably due to interactions involving the cell wall β-glucan. Thus, this study provides a new modification method for PAA surfaces and shows that it can be used to induce selective adsorption of proteins and microorganisms.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.