Abstract
The ordered ω phase in as-cast Ti-45Al-8.5Nb-0.2B alloy and its phase transformation during heat treatment are investigated. Ordered ω variants are observed to uniformly precipitate within the βo area in as-cast Ti-45Al-8.5Nb-0.2B alloy. After annealing at 850 °C for 500 h, the βo areas are replaced by large B82-ωo grains. Small γ precipitates are observed at the grain boundaries of the ωo phase and are thought to be transformed from the βo phase. Moreover, the ωo precipitates directly transformed from the parent α2 laths are found within the lamellar colonies. The orientation relationship between the ωo phase and the lamellar structure is < 110]γ//[0001]ωo//[112¯ 0]α2; (111)γ//(112¯ 0)ωo//(0001)α2. The interfaces between the ωo and γ are semi-coherent. The ωo phase is an equilibrium phase at 850 °C in high Nb-containing TiAl alloys. When annealed at 1250 °C, the ordered ω is eliminated in a short time, and the βo phase is substituted by the coarsened α2 laths in the lamellar colonies after 12 h annealing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.