Abstract
Vanadis 6 cold work tool steel was vacuum austenitized, room temperature quenched, differently cryogenically treated (-75, -140 and -196 °C for different durations) and double tempered, at temperatures of either 170 or 530 °C. Galling resistance was assessed by pin-on-disc testing of differently treated specimens against CuSn bronze, at wide ranges of sliding velocities and loads. The obtained results show that cryogenic treatments combined with low temperature tempering improves anti-galling performance of the steel. The best tribological properties were obtained when high-temperature tempering was combined with cryogenic treatment at -196 °C, due to the maximum extent of microstructural alteration generated by this kind of treatment. The improvement in wear performance is accompanied with slight but undisputable increase in corrosion resistance of the steel, at almost no affected toughness as compared with the state after conventional heat treatment. In conclusion, the obtained results imply an opportunity to simultaneously improve wear performance, corrosion resistance and toughness of the examined steel, by choosing a proper combination of cryogenic treatment and tempering.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.