Abstract
Magnesium hydride is extensively examined as a hydrogen store due to its high hydrogen content and low cost. However, high thermodynamic stability and sluggish kinetics hinder its practical application. To overcome this last drawback, different Ti amounts (y = 0, 0.025, 0.05, 0.1, 0.2 and 0.3) were added to magnesium to form (1-y)MgH2+yTiH2 nanocomposites (NC) by reactive ball milling under hydrogen gas. Thermodynamic stability of the MgH2 phase in NCs was determined using a manometric Sieverts rig. Reversible hydrogen capacity and reaction kinetics were determined at 573 K over 20 sorption cycles under a limited reaction time of 15 min. On increasing Ti amount, reaction kinetics are enhanced both in absorption and desorption leading to a higher reversibility for hydrogen storage with the MgH2 phase. However, titanium increases the molar weight of NCs and forms irreversible titanium hydride. The highest reversible capacity (4.9 wt% H) was obtained for the lowest here studied TiH2 content (y = 0.025).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.