Abstract
AbstractMany processing parameters can be adjusted to optimize the fused filament fabrication (FFF) process, a popular and widely used additive manufacturing techniques for plastic materials. Among those easily adjusted parameters are the nozzle temperature, printing speed, raster orientation, and layer thicknesses. Using poly(ether ether ketone) (PEEK) as the base material, a design of experiments analysis was performed on the main FFF parameters. A response surface methodology was applied to analyze the results and to maximize the output responses. Results have shown that the nozzle temperature is the most influential parameter on tensile properties and the crystallinity degree of printed PEEK by FFF process. Parts produced with optimized FFF parameters were then subjected to an annealing treatment to induce a relaxation of residual stress and to enhance crystallinity. The best properties for 3D printed PEEK parts were achieved with annealed parts prepared at 400°C with a printing speed of 30 mm/s, 0.15 mm layer thickness and raster orientation of [0°/15°/−15°]. The resulting parts have mechanical properties comparable to those of injected PEEK.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.