Abstract
400-nm-thick (Pb,La)(Zr,Ti)O 3 (PLZT) films with a composition of Pb:La:Zr:Ti = X:3:65:35 were fabricated on (111)Pt/Ti/SiO 2 /(100)Si substrates at 700°C by chemical solution deposition using precursor solutions with Pb contents of X = 107, 112, 116, 121 and 126. The PLZT films fabricated from the solutions of X = 107 and 112 had bimodal structure and included pyrochlore phase. The pyrochlore region decreased with increasing the Pb content, and single perovskite phase PLZT films with well-filled structure were obtained at the Pb contents of 121 and 126. From these results, we concluded that the Pb-content of X = 121 (125 mol% relative to a stoichiometric value) was optimum for the fabrication of PLZT films for optical applications. This optimization slightly improved electrical and electrooptic properties of the PLZT films, and finally the PLZT(121/3/65/35) film showed the Pockels coefficient of 84 pm/V.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.