Abstract
Magnetic properties and high frequency characteristics of binary Co100−xTax (x = 0–24) thin films, prepared by using the oblique sputtering method under an external magnetic field of 1200 Oe have been studied. All the Co100−xTax films are easy to form amorphous phase, and thus exhibit strong in-plane uniaxial magnetic anisotropy, high resistivity, and low coercivity. With increasing x, the saturation magnetization (4πMs) and coercivity along the easy and hard axes (Hce and Hch) are decreased, while the magnetic anisotropy field (Hk) reaches the maximum value of 578 Oe for the films with the composition to become fully amorphous phase. Due to large Hk, high ferromagnetic-resonance frequency (fFMR) of 4.7–6.6 GHz is obtained for Co100−xTax (x = 11–24) films. The optimal magnetic properties of 4πMs = 10.9 kG, Hce = 6.2 Oe, Hch = 6.0 Oe, Hk = 507 Oe, and high resonance characteristics of fFMR = 6.4 GHz, respectively, are reached for Co84Ta16 films. Finally, high fFMR of 5.4–7.2 GHz and Hk of 434–617 Oe can be tuned by the modification of the sputtering parameters. This result reflects the benefit of Co100−xTax (x = 11–22) films for above 5 GHz applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.