Abstract
ABSTRACTZnO nanorods were synthesized by chemical solution method at low temperature. The surface of nanorods was changed to porous by using thermal annealing and chemical etching. Surface morphology and their optical properties were changed according to annealing and etching condition. Photoluminescence from as-grown ZnO nanorods almost showed defect related emission in wide range from 450∼900 nm. After annealing at 500°C, the band-edge emission of ZnO was observed and emission at visible range was changed to green with decreasing red-orange. The surface morphology of ZnO nanorods was transformed to porous by chemical etching and it led to increase the intensity of band-edge emission about three times. The internal quantum efficiency for porous ZnO nanorods, which was calculated from ratio PL intensity at 10K and 300K, is about 21%. Also, the random lasing at porous ZnO nanorods was occurred at high optical excitation by a photon with traveling inside or outside of porous ZnO nanorod gets amplified by injection second photon before leaving porous ZnO nanorods.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.