Abstract
Nickel based materials are the most potential catalysts for COx-free hydrogen production from ammonia decomposition. However, the facile synthesis of supported Ni-based catalysts with small size Ni particles, high porosity and good structural stability is still of great demand. In this work, uniform small-sized Ni particles supported into porous alumina matrix (Ni@Al2O3) are synthesized by a simple one-pot method and used for ammonia decomposition. The Ni content is controlled from 5 at.% to 25 at.%. Especailly, the 25Ni@Al2O3 catalyst shows the best catalytic performance. With a GHSV of 24,000 cm3gcat−1h−1, 93.9% NH3 conversion is achieved at 600 °C and nearly full conversion of NH3 is realized at 650 °C. The hydrogen formation rate of 25NiAl catalyst reaches 3.6 mmol gcat−1min−1 at 400 °C and 7.8 mmol gcat−1min−1 at 450 °C. The enhanced activity observed on 25Ni@Al2O3 catalyst can be attributed to the structural characteristic that large amounts of uniform-sized small (7.2 ± 0.9 nm) Ni particles are highly dispersed into porous alumina matrix. The aggregation of active metallic Ni particles during the high temperature reaction can be effectively prevented by the porous alumina matrix due to the strong interaction between them, thus ensuring a good catalytic performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.