Abstract
Tungsten bronze (MxWO3) materials have been widely used as thermal insulation for architectural glass because of their higher near-infrared (NIR) light shielding capacity. To solve the problems encountered in solvothermal preparation with high costs and low yields, this study has developed a facile, eco-friendly, effective, but low-cost method, with no need for any annealing process, for promoting the large-scale fabrication of cesium tungsten bronze (CsxWO3, x = 0.32) nanomaterials for potential thermal insulation windows applications. In the proposed ball-milling process, the tungstic acid material could be reduced to hydro tungsten bronze (HxWO3) by cellulose, while the cesium ions (Cs+) could be gradually incorporated into the interspace until the formation of Cs0.32WO3 (Cs/W atomic ratio = 0.32), with an average particle size of ∼33 nm after a 15 h ball-milling process. The reaction mechanism has been investigated in detail via particle structural analysis and optical performance characterization. The obtained Cs0.32WO3 nanoparticles are dispersed in a solution composed of surfactant (s) and polymer (s) which can form a thin film with a thickness of about 2 μm on a glass substrate, by a spinning coating or casting method, to exhibit high visible (Vis) light transmittance (T566nm = 72.6%), and excellent NIR-shielding capability (T1388nm = 5.3%), reflected by good heat-insulating performance in practice use. This work will pave a new path for large-scale production of Cs0.32WO3 nanomaterials with low costs and high performance, beneficial for practical applications in energy-saving glass coatings.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.