Abstract
Effect of Ni addition on structural properties and, cation distribution of Zn0.75-xNixMg0.15Cu0.1Fe2O4 (x = 0.0, 0.15, 0.30, 0.60, 0.75) ferrites, prepared using sol-gel autocombustion method was studied using X-ray diffraction (XRD) technique. XRD analysis reveals the formation of spinel phase even in dry gel form. The lattice constant (aexp.) decreases with Ni2+ substitution and follows Vegard's law. Scherrer's grain diameter (D) lies within the range of 17.33 - 26.47 nm. Due to difference in the ionic radii of Zn2+ and Ni2+ significant changes are observed in the structural parameters - unit cell volume (V), hopping length at A (La) and B (Lb) site, and x-ray density (ρXRD). Linear increase in Neel magnetic moment (nBN) with oxygen positional parameter is observed in the studied samples, attributed to simultaneous weakening of A-B interaction and strengthening of the B-B interaction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.