Abstract
Structures externally rehabilitated with fiber reinforced plastics (FRP) are often exposed to aggressive environmental conditions that dictate deterioration mechanisms and shorten their structural life-cycle. That degradation and ensuing failure may be due to a combination of factors and the environmental conditions leading to such failures include cyclic temperature variation, sorption of saline moisture due to salt fogging or dry-wet cycles and immersion in water.This study seeks to contribute to better knowledge of the phenomena involved, by studying degradation of GFRP laminates through tests of mechanical strength after accelerated aging designed to estimate long term natural degradation. The measured degradation is extrapolated to other environmental situations likely to occur for longer periods using Arrhenius type of analysis. The validity of the generalizations based on parameters derived from diffusion studies or from the tensile strength tests is examined.It is preliminarily concluded that Arrhenius equations based on experiments made after salt fogging at 30°C, 45°C and 55°C are not applicable. The extrapolations based on diffusion laws were found unsuccessful. However it was possible to extend the results after accelerated aging to prototype conditions in the case of immersion in salt water by application of Arrhenius methods.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.