Abstract
A series of Zr1-xNixO2 nanocrystalline powders were synthesized by chemical route and then calcined at 750 °C for 5 h. A mixed phase of monoclinic and tetragonal phase of ZrO2 has been observed in XRD patterns and Raman studies. The tetragonal phase of ZrO2 increases up to a Ni concentration of x = 0.025 and thereafter suppression of the tetragonal phase is observed with the increase in monoclinic phase of ZrO2. At lower concentration of Ni of x = 0.01, the material manifests with diamagnetic property and then a diamagnetic to ferromagnetic transition is established at above than x = 0.01. The saturation magnetization increases with increase in Ni concentration up to x = 0.025 and then decreases for Ni concentration of x = 0.03 in Ni substituted ZrO2. The sudden fall in saturation magnetization in Zr0.97Ni0.03O2 arises due to the superexchange interactions between two neighboring Ni2+ ions which lead to antiferromagnetism in the material and suppress the ferromagnetic ordering.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.