Abstract
Symmetric GaGdN/AlGaN (Gd concentration: 2%) and GaN/AlGaN double quantum well superlattices (DQW-SLs) were grown by radio-frequency plasma-assisted molecular-beam epitaxy on GaN (0001) templates. Atomic steps were observed on all the sample surfaces by atomic force microscope. X-ray diffraction θ/2θ scan curves exhibited well-defined satellite structures. Room temperature ferromagnetism was confirmed for the GaGdN/AlGaN DQW-SL samples by using alternating gradient magnetometer. Strong photoluminescence was observed from both GaGdN and GaN QWs at higher energy side of GaN excitonic peak. Magneto-photoluminescence spectra for GaGdN/AlGaN DQW-SL samples showed a large magnetic field dependence of the excitonic energy by applying a magnetic field up to 7T. The observed strong redshift of excitonic PL indicated an enhancement of Zeeman splitting of the free carrier energy levels in magnetic GaGdN/AlGaN DQW-SL. Enhanced g-factor was estimated to be about 60 for GaGdN/AlGaN DQW-SL sample with QW thickness of 1nm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.