Abstract
Gradient-structured ternary Fe-Co-Ni alloy coatings electrodeposited on steel substrates at various current densities from chloride baths were numerically and experimentally investigated. The electrodeposition process, considering hydrogen evolution and hydrolysis reaction, was modelled using the finite element method (FEM) and was based on the tertiary current distribution. The experimentally tested coating thickness and elemental contents were used to verify the simulation model. Although there was a deviation between the simulation and experiments, the numerical model was still able to predict the variation trend of the coating thickness and elemental contents. The influence of the current density on the coating characterization was experimentally studied. Due to hydrogen evolution, the coating surface exhibited microcracks. The crack density on the coating surface appeared smaller with increasing applied current density. The XRD patterns showed that the deposited coatings consisted of solid-solution phases α-Fe and γ (Fe, Ni) and the metallic compound Co3Fe7; the current density in the present studied range had a small influence on the phase composition. The grain sizes on the coating surface varied from 15 nm to 20 nm. The microhardness of the deposited coatings ranged from 625 HV to 655 HV. Meanwhile, the average microhardness increased slightly as the current density increased from 5 A/dm2 to 10 A/dm2 and then decreased as the current density further increased. Finally, the degree of anomaly along with the metal ion and hydrogen atom concentrations in the vicinity of the cathodic surface were calculated to investigate the anomalous codeposition behaviour.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have