Abstract
A new dianhydride 9,10-diphenyl-9,10-bis(trifluoromethyl)-9,10-dihydroanthracene-2,3,6,7-tetraacid dianhydride (6FDPDA) with rigid semi-alicyclic structure was reported. CPI materials were prepared by copolymerizing 6FDPDA with 3,3′,4,4′-biphenyl tetracarboxylic dianhydride (BPDA) or 4,4’-(hexafluoroisopropene) diphthalic anhydride (6FDA) respectively, with 2,2′-bistrifluoromethyl benzidine (TFDB) as the diamine building blocks. Due to the ladder semi-alicyclic structure as well as –CF3 and phenyl large side groups, this new dianhydride exhibits two important advantages, the cut-off conjugated in the polymer backbone and suppressed intermolecular stacking. When 6FDA as the dianhydride comonomer, the obtained CPIs exhibits distinguished performance with transmission of 90 % at 550 nm, YI of 2.45, CTE of 16.5 ppm/K and Tg over 450 °C. These results demonstrated that 6FDPDA is an excellent building block to prepare the high performance CPIs in optoelectronic devices, for an example the substrates for flexible AMOLED display.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.