InGaPBi crystalline thin films with up to 2.1% bismuth concentration have been grown on GaAs substrates by molecular beam epitaxy. Rutherford backscattering spectrometry confirms that the majority of Bi atoms are located at substitutional lattice sites. The films exhibit good surface, structural, and interface quality, and their strains can be tuned from tensile to compressive by increasing the Bi content. InBi LO and GaBi LO vibrational modes in Raman spectroscopy were observed, and their intensities increased with Bi concentration. A weak photoluminescence signal was observed at 1.78 eV at room temperature for the sample with a Bi content of 0.5%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.